Magnesia chrome brick five performance

Magnesia chrome brick is made of some preliminary synthesis high purity raw materials. The high purity raw refractories should be high pressure formed, ultra high temperature fired and then go through some other post-treatment process and system, finally made the magnesite chrome brick.

Magnesia chrome brick five performance:
1 chemical composition and mineral composition 
Magnesia chrome brick chemical composition with the choice of raw materials vary. General magnesium oxide total of 55% to 60%, chromium oxide is about 10%, followed by ferric oxide and a small amount of aluminum dioxide, silica, calcium oxide and other impurities.
Magnesia chrome refractory bricks mineral composition is mainly magnesium chrome spinel and magnesium ferrite.
2 refractoriness
As the magnesia chrome fire bricks magnesium content less than magnesium bricks, magnesium chrome spinel and magnesium ferrite content, and their eutectic compound melting point is relatively low, so the magnesia chrome brick china refractory  magnesia, generally only 1850 ~ 1960 ℃.
3 load softening temperature
Magnesite in the magnesia-chrome brick and magnesium-chromium spinel is easy to form a mesh skeleton, because the low melting point filled in the network gap is less material, when the high temperature load, although the low melting point softening, Skeleton can still support the load, so the magnesia chrome bricks softening temperature is higher, generally up to 1550 ℃ or more. The refractoriness is slightly lower than that of the magnets and the softening temperature is higher than that of the magnets.
4 Thermal expansion and thermal shock stability
Magnesium chrome tungsten chrome spinel and magnesium ferrite content and linear expansion coefficient is small, at the same time, magnesium chrome brick porosity than magnesium bricks, so the MgO Cr brick thermal expansion is small.
Magnesia-chrome brick calcium perovskite content is very small, not easy to cause the expansion of the expansion of stress; magnesium ferrite dissolved in the magnesium chrome spinel, the solubility of large two dissolved temperature range is also wide, the melting and precipitation of magnesium ferrite , And will not produce large stress, therefore, magnesia chrome brick thermal shock stability is better, the number of water up to 25 times.
5 slag resistance
Magnesia chrome brick in the content of more magnesium chrome spinel is magnesium oxide and chromium oxide complex, and chromium trioxide is a typical neutral oxide, therefore, magnesium chrome brick on the alkaline, acidic slag erosion Have a strong resistance.
Yingkou Ruizhi Refractories Co., Ltd. is a professional China manufacturer of refractory material for high temperature melting furnaces.Ruizhi Refractories supply main products are: china refractory materials, refractory brick, refractory castable,refractory nozzle, ceramic fiber, fire brick, insulation material, for converter, electric arc furnace, ladle, LF furnace, tundish, foundry ladle, torpedo ladle, etc. Ruizhi has established technical cooperation relationship with some refractory research institutions and universities. Ruizhi Refractories products have been exported to such as South Africa, Australia, Canada, Malaysia, Bangladesh, Iran, Saudi Arabia, UAE, Iraq, Pakistan, Philippines, Vietnam, Singapore, Tajikistan, Indonesia, South Korea, Sri Lanka, Nigeria, Kenya, Ethiopia, etc.